EPC-NS
Electrically Conductive Polymer Composition with Low Resistance
Description
Description: Electrically conductive polymer composition with low specific volume resistance.
Application: Intended for extrusion. Can be used to create conductive polymer structures as well as monitoring layers in cable products.
TU 2243-004-63892139-14
Technical Specifications:
| Parameter | Value | Method |
| Density, g/cm³ | 1,13 | GOST IEC 60811 |
| Melt Flow Rate (MFR), g/10 min | 2,2 | GOST IEC 60811 |
| Tensile Strength, MPa | 12,1 | GOST IEC 60811 |
| Elongation at Break, % | 120 | GOST IEC 60811 |
| Удельное объемное электрическое сопротивление при 23 °С, Ом·см | 2,7 | GOST 20214 |
| Specific Volume Resistance at 23 °C, Ω*cm | 96 ÷ 98 | ASTM D 2240 |
| Main impurity content, ‰ no more than | 0,06 ÷ 0.08 | ASTM D 6980 |
Processing Modes:
- Drying (recommended): 60–70 °C
- Processing Temperature Profile: 110 – 130 – 135 – 140 – 150 °C
Storage Conditions: Store in a closed room, avoiding direct sunlight, at a temperature of 10 to 35 °C and humidity of 40-70%.
Shelf Life: 1 year from the date of production, the composition should be stored in a warm room, avoiding direct sunlight, at a temperature not lower than 10 °C for at least 24 hours. The material is packed in corrugated cardboard octabins with a net material weight of 900 kg (with a PE liner inside) or in 25 kg bags.