EPC-NG
Flame-retardant electrically conductive polymer composition free of halogens
Description
Description: A flame-retardant polymer thermoplastic composition that does not contain halogens.
Application: A flame-retardant electrically conductive thermoplastic composition with a processing temperature in the range of 110-150 °C. Recommended processing method is extrusion. It can be used for the extrusion of conductive polymer coatings over flame-retardant substrates or "HF" compositions to create control layers.
TU 20.16.59—005-93982943-2019
Technical Characteristics:
| Property | Test Results | Testing Methods |
| Density, g/cm³ | 1,13 | GOST IEC 60811 |
| Melt Flow Rate (MFR), g/10 min (190°C, 5 kg) | 2 ÷ 4 | GOST IEC 60811 |
| Tensile strength, MPa | 12,3 | GOST IEC 60811 |
| Elongation at break, % | 130 | GOST IEC 60811 |
| Volume resistivity, no more than, Ω·cm | 6,7 | GOST 20214 |
| Shore hardness, A | 96 ÷ 98 | ASTM D 2240 |
| Ignition temperature, °C | 0,07 ÷ 0.09 | ASTM D 6980 |
| Vicat softening temperature, °C | 26 ÷ 27 | GOST 21793 |
Processing Conditions:
- Drying (recommended): 60-70 °C
- Extrusion processing temperature: 110-115 °C, 125-130 °C, 135-140 °C, 150 °C
Storage Conditions: Recommended to store in a closed room, avoiding direct sunlight, at a temperature from 10 °C to 35 °C and humidity of 40-70%.
Guarantees: Minimum shelf life of materials, provided they are stored in a dry closed room at a temperature no lower than 10 °C for at least 24 hours.
Before processing, the material should be kept in a warm room at a temperature no lower than 10 °C for at least 24 hours.
Packing and transportation of the weighing material on pallets no more than 900 kg (PE packaging inside) or bags of 25 kg